Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa
Preparation of cellulose acetate (CA) membranes with ultrafiltration process had be done by phase inversion using dimethylformamide (DMF) as solvent. Poliethylene glycol (PEG) 1450 Da, as additive, was added with 10, 20, and 30% rasio of celluose acetate. The thin film of polymer solution was immers...
Saved in:
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universitas Syiah Kuala, Chemical Engineering Department
2012-06-01
|
| Series: | Jurnal Rekayasa Kimia & Lingkungan |
| Online Access: | https://jurnal.usk.ac.id/RKL/article/view/250 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1849432383010373632 |
|---|---|
| author | Cut Meurah Rosnelly |
| author_facet | Cut Meurah Rosnelly |
| author_sort | Cut Meurah Rosnelly |
| collection | DOAJ |
| description | Preparation of cellulose acetate (CA) membranes with ultrafiltration process had be done by phase inversion using dimethylformamide (DMF) as solvent. Poliethylene glycol (PEG) 1450 Da, as additive, was added with 10, 20, and 30% rasio of celluose acetate. The thin film of polymer solution was immersed on water bath coagulation at room temperature. The analysis of membrane morphology structure by Scanning Electron Microscope (SEM) JSM – 5310 LV, Jeol-Japan showed the asymetric of membrane. The addition of PEG can improve the performance of the membrane. In resulting flux is higher than membranes without PEG. Increasing of PEG/CA ratio resulted in the higher flux with lower of rejection. The higher fluxes of water, dextran, and BSA are 146, 114, and 96 L/m2hr with 52,938 and 75,716% rejection for dextran and BSA.
Keywords: cellulose acetate membranes, polyethylene glycol, ultrafiltration |
| format | Article |
| id | doaj-art-e295fbc5786c42e683403af31584b1ac |
| institution | Kabale University |
| issn | 1412-5064 2356-1661 |
| language | English |
| publishDate | 2012-06-01 |
| publisher | Universitas Syiah Kuala, Chemical Engineering Department |
| record_format | Article |
| series | Jurnal Rekayasa Kimia & Lingkungan |
| spelling | doaj-art-e295fbc5786c42e683403af31584b1ac2025-08-20T03:27:22ZengUniversitas Syiah Kuala, Chemical Engineering DepartmentJurnal Rekayasa Kimia & Lingkungan1412-50642356-16612012-06-01912529245Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi FasaCut Meurah Rosnelly0Jurusan Teknik Kimia Fakultas Teknik Universitas Syiah KualaPreparation of cellulose acetate (CA) membranes with ultrafiltration process had be done by phase inversion using dimethylformamide (DMF) as solvent. Poliethylene glycol (PEG) 1450 Da, as additive, was added with 10, 20, and 30% rasio of celluose acetate. The thin film of polymer solution was immersed on water bath coagulation at room temperature. The analysis of membrane morphology structure by Scanning Electron Microscope (SEM) JSM – 5310 LV, Jeol-Japan showed the asymetric of membrane. The addition of PEG can improve the performance of the membrane. In resulting flux is higher than membranes without PEG. Increasing of PEG/CA ratio resulted in the higher flux with lower of rejection. The higher fluxes of water, dextran, and BSA are 146, 114, and 96 L/m2hr with 52,938 and 75,716% rejection for dextran and BSA. Keywords: cellulose acetate membranes, polyethylene glycol, ultrafiltrationhttps://jurnal.usk.ac.id/RKL/article/view/250 |
| spellingShingle | Cut Meurah Rosnelly Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa Jurnal Rekayasa Kimia & Lingkungan |
| title | Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa |
| title_full | Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa |
| title_fullStr | Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa |
| title_full_unstemmed | Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa |
| title_short | Pengaruh Rasio Aditif Polietilen Glikol Terhadap Selulosa Asetat pada Pembuatan Membran Selulosa Asetat Secara Inversi Fasa |
| title_sort | pengaruh rasio aditif polietilen glikol terhadap selulosa asetat pada pembuatan membran selulosa asetat secara inversi fasa |
| url | https://jurnal.usk.ac.id/RKL/article/view/250 |
| work_keys_str_mv | AT cutmeurahrosnelly pengaruhrasioaditifpolietilenglikolterhadapselulosaasetatpadapembuatanmembranselulosaasetatsecarainversifasa |