A Comparative Study on Corrosion Fatigue Susceptibility and Microstructural Effects in 6061-T6 and 6082-T6 Aluminum Alloys

A Comparative Study on Corrosion Fatigue Susceptibility and Microstructural Effects in 6061-T6 and 6082-T6 Aluminum Alloys

In the present study, fatigue performance of 6061-T6 and 6082-T6 commercially available extruded aluminum alloys in dry air and 3.5 wt% NaCl-saturated environment was investigated and compared. It was found that the aggressive chloride environment accelerated fatigue failure by up to an order of mag...

Full description

Saved in:
Bibliographic Details
Main Authors: Tetiana Avramenko, Silvain Michel, Alex Stutz, Jan Kollender, Iurii Burda, Ulrik Hans, Christian Affolter, Giovanni Pietro Terrasi
Format: Article
Language:English
Published: MDPI AG 2025-06-01
Series:Metals
Subjects:
6061-T6 alloy
6082-T6 alloy
corrosion fatigue
pitting corrosion
microstructure
Online Access:https://www.mdpi.com/2075-4701/15/6/653
Tags: Add Tag
No Tags, Be the first to tag this record!

Internet

https://www.mdpi.com/2075-4701/15/6/653

Similar Items