Phase equilibria of the Al-Co-Er system at 400°C and 600°C
The 400°C and 600°C isothermal sections of the Al–Co–Er system were studied assisted with X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA) techniques. 18 three-phase fields were identified in the 400°C isothermal section. The maximum solid solubili...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Belgrade, Technical Faculty, Bor
2021-01-01
|
| Series: | Journal of Mining and Metallurgy. Section B: Metallurgy |
| Subjects: | |
| Online Access: | http://www.doiserbia.nb.rs/img/doi/1450-5339/2021/1450-53392100032Z.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The 400°C and 600°C isothermal sections of the Al–Co–Er system were studied assisted with X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA) techniques. 18 three-phase fields were identified in the 400°C isothermal section. The maximum solid solubilities of Al in Co3Er and Co2Er were 13.93 at.%, and 16.13 at.%, respectively whereas the maximum solid solubilities of Co in Al2Er, Al2Er3 and AlEr2 were 6.93 at.%, 6.65 at.%, and 6.49 at.%, respectively. The solid solution range of λ is from 22.22 at.% Al to 44.44 at.% Al while the 600°C isothermal section included 20 three-phase fields. The maximum solid solubilities of Al in Co17Er2 and Co7Er2 were 10.17 at.% and 10.24 at.%, respectively. The maximum solid solubilities of Co in Al2Er and Al2Er3 were 3.63 at.% and 2.01 at.%, respectively. |
|---|---|
| ISSN: | 1450-5339 2217-7175 |