Characteristics of Separations in Fracture After Crack Tip Opening Displacement Tests of Low-Carbon Microalloyed Offshore Steel S460MLO

Characteristics of Separations in Fracture After Crack Tip Opening Displacement Tests of Low-Carbon Microalloyed Offshore Steel S460MLO

Using the results from testing industrial batches of 23 mm steel heavy plates after thermomechanical rolling and subsequent post-weld heat treatment, the patterns of fatigue crack formation in the fracture specimens during CTOD (Crack Tip Opening Displacement) testing for fracture toughness are inve...

Full description

Saved in:
Bibliographic Details
Main Authors: Eugene Goli-Oglu, Marco Palombo, Andrei Filatov
Format: Article
Language:English
Published: MDPI AG 2025-04-01
Series:Alloys
Subjects:
low-carbon steel
heavy plate
fatigue
crack opening displacement
fracture toughness
separations
Online Access:https://www.mdpi.com/2674-063X/4/2/6