Role of CA-EDTA on the Synthesizing Process of Cerate-Zirconate Ceramics Electrolyte
The role of a combination between citric acid (CA) and ethylenediaminetetra acetic acid (EDTA) as chelating agents in preparation of BaCe0.54Zr0.36Y0.1O2.95 powder by a modified sol-gel method is reported. The precursor solutions were prepared from metal nitrate salts (M+), chelating agents (C), and...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2013-01-01
|
| Series: | Journal of Chemistry |
| Online Access: | http://dx.doi.org/10.1155/2013/908340 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The role of a combination between citric acid (CA) and ethylenediaminetetra acetic acid (EDTA) as chelating agents in preparation of BaCe0.54Zr0.36Y0.1O2.95 powder by a modified sol-gel method is reported. The precursor solutions were prepared from metal nitrate salts (M+), chelating agents (C), and ethylene glycol (EG) at molar ratio of M+ : C : EG = 3 : 2 : 3. Chemical and phase transformation of samples during thermal decomposition were analyzed by thermogravimetric analysis (TGA) and Fourier transform infrared (FTIR) spectroscopy. TGA results show that the sample prepared by a combination of CA-EDTA exhibited the lowest thermal decomposition temperature, Ttd since there was no significant weight loss after 750°C. After calcined at 1100°C, the carbonates residue remained in the samples as proven by FTIR results. It was found that the used combination of CA-EDTA acts as a better combustion reagent to increase the reaction rate and influence the thermal decomposition behaviour compared to a single citric acid and EDTA, respectively. Apparently, calcination temperatures above 1100°C are needed to produce a pure perovskitic BaCe0.54Zr0.36Y0.1O2.95. |
|---|---|
| ISSN: | 2090-9063 2090-9071 |