Multispecies colonisation and surface erosion on A106 GB industry-finished steel used in heat exchangers
Multispecies bacterial attachment to carbon steel surfaces is not fully understood; for example, as to why the attachment of certain bacteria influences corrosion. In this study, finished steel, A 106 GB was exposed to a mixed bacterial culture in a batch reactor system at a constant temperature of...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor & Francis Group
2024-12-01
|
| Series: | Biotechnology & Biotechnological Equipment |
| Subjects: | |
| Online Access: | https://www.tandfonline.com/doi/10.1080/13102818.2024.2326292 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Multispecies bacterial attachment to carbon steel surfaces is not fully understood; for example, as to why the attachment of certain bacteria influences corrosion. In this study, finished steel, A 106 GB was exposed to a mixed bacterial culture in a batch reactor system at a constant temperature of 35 °C to evaluate the corrosion rate with and without bacterial influence. Cultures collected from the cooling tower site were exposed to coupons and were grown in a batch reactor. Atomic force microscopy (AFM) was used to obtain roughness parameters. Surface morphology and colonisation patterns were observed by scanning electron microscopy (SEM). 16S rDNA sequencing indicated predominance of Pseudomonas sp. and Clostridium sp. on the rough surfaces. Cell colonisation of surfaces showed no time-related differences, with differences observed on surface roughness parameters. Intergranular and uniform corrosion was observed. The smooth finished steel surface performed best in resisting corrosion. |
|---|---|
| ISSN: | 1310-2818 1314-3530 |