Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys
In order to find out the best film forming temperature of pure lanthanum salt conversion film on the surface of magnesium alloy, lanthanum salt conversion film was prepared on the surface of magnesium alloy at different film forming temperatures. Scanning electron microscopy (SEM), energy dispersive...
Saved in:
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Department of Materials Protection
2021-04-01
|
| Series: | Cailiao Baohu |
| Subjects: | |
| Online Access: | http://www.mat-pro.com/fileup/1001-1560/PDF/20210417.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1850118780680667136 |
|---|---|
| author | XU Man - zu, ZOU Zhong - li |
| author_facet | XU Man - zu, ZOU Zhong - li |
| author_sort | XU Man - zu, ZOU Zhong - li |
| collection | DOAJ |
| description | In order to find out the best film forming temperature of pure lanthanum salt conversion film on the surface of magnesium alloy, lanthanum salt conversion film was prepared on the surface of magnesium alloy at different film forming temperatures. Scanning electron microscopy (SEM), energy dispersive x - ray spectrometer (EDS) and X - ray diffraction (XRD) were used to observe and analyze the surface morphology and composition of the film, the corrosion resistance of the coating was studied by drop test and electrochemical method. Results showed that lanthanum salt conversion film was formed on the surface of magnesium alloy, and there were cracks with different sizes on the surface of the samples under the different film forming temperatures, among which the surface cracks of lanthanum salt conversion film obtained at 20 ℃ were the least; EDS results showed that the lanthanum salt conversion film on the surface of magnesium alloy was mainly composed of La and O elements, XRD results showed that lanthanum hydroxide was the main component of the conversion film; The results of drop experiment showed that the lanthanum salt conversion film obtained at 20 ℃ had the best corrosion resistance, and the electrochemical test results were consistent with the drop experiment results. Compared with the untreated magnesium alloy samples, the self - corrosion potential shifted 865 mV positively, the self - corrosion current density was decreased by 4 orders of magnitude, and the impedance modulus was increased by about 4 orders of magnitude. |
| format | Article |
| id | doaj-art-df1722426a4649c8b5b91e95cf4d738b |
| institution | OA Journals |
| issn | 1001-1560 |
| language | zho |
| publishDate | 2021-04-01 |
| publisher | Editorial Department of Materials Protection |
| record_format | Article |
| series | Cailiao Baohu |
| spelling | doaj-art-df1722426a4649c8b5b91e95cf4d738b2025-08-20T02:35:47ZzhoEditorial Department of Materials ProtectionCailiao Baohu1001-15602021-04-01544909310.16577/j.cnki.42-1215/tb.2021.04.017Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium AlloysXU Man - zu, ZOU Zhong - li0(School of Materials Science and Engineering, North Minzu University, Yinchuan 750021, China)In order to find out the best film forming temperature of pure lanthanum salt conversion film on the surface of magnesium alloy, lanthanum salt conversion film was prepared on the surface of magnesium alloy at different film forming temperatures. Scanning electron microscopy (SEM), energy dispersive x - ray spectrometer (EDS) and X - ray diffraction (XRD) were used to observe and analyze the surface morphology and composition of the film, the corrosion resistance of the coating was studied by drop test and electrochemical method. Results showed that lanthanum salt conversion film was formed on the surface of magnesium alloy, and there were cracks with different sizes on the surface of the samples under the different film forming temperatures, among which the surface cracks of lanthanum salt conversion film obtained at 20 ℃ were the least; EDS results showed that the lanthanum salt conversion film on the surface of magnesium alloy was mainly composed of La and O elements, XRD results showed that lanthanum hydroxide was the main component of the conversion film; The results of drop experiment showed that the lanthanum salt conversion film obtained at 20 ℃ had the best corrosion resistance, and the electrochemical test results were consistent with the drop experiment results. Compared with the untreated magnesium alloy samples, the self - corrosion potential shifted 865 mV positively, the self - corrosion current density was decreased by 4 orders of magnitude, and the impedance modulus was increased by about 4 orders of magnitude.http://www.mat-pro.com/fileup/1001-1560/PDF/20210417.pdflanthanum nitrate; chemical conversion film; film forming temperature; magnesium alloy; corrosion resistance |
| spellingShingle | XU Man - zu, ZOU Zhong - li Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys Cailiao Baohu lanthanum nitrate; chemical conversion film; film forming temperature; magnesium alloy; corrosion resistance |
| title | Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys |
| title_full | Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys |
| title_fullStr | Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys |
| title_full_unstemmed | Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys |
| title_short | Effects of Film Forming Temperature on Corrosion Resistance of Lanthanum Salt Conversion Film on Magnesium Alloys |
| title_sort | effects of film forming temperature on corrosion resistance of lanthanum salt conversion film on magnesium alloys |
| topic | lanthanum nitrate; chemical conversion film; film forming temperature; magnesium alloy; corrosion resistance |
| url | http://www.mat-pro.com/fileup/1001-1560/PDF/20210417.pdf |
| work_keys_str_mv | AT xumanzuzouzhongli effectsoffilmformingtemperatureoncorrosionresistanceoflanthanumsaltconversionfilmonmagnesiumalloys |