Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel
Martensitic medium‐Mn steels have attracted significant attention for their excellent ultimate tensile strength, high ductility, and low austenitizing temperatures but remain susceptible to hydrogen embrittlement (HE). In this study, we investigated the role of ε carbides formed during paint baking...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2025-07-01
|
| Series: | Journal of Materials Research and Technology |
| Subjects: | |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785425017405 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1849413102392573952 |
|---|---|
| author | Jin-Young Lee Hyun-Bin Jeong Won Hui Jo Jae Bok Seol Young-Kook Lee |
| author_facet | Jin-Young Lee Hyun-Bin Jeong Won Hui Jo Jae Bok Seol Young-Kook Lee |
| author_sort | Jin-Young Lee |
| collection | DOAJ |
| description | Martensitic medium‐Mn steels have attracted significant attention for their excellent ultimate tensile strength, high ductility, and low austenitizing temperatures but remain susceptible to hydrogen embrittlement (HE). In this study, we investigated the role of ε carbides formed during paint baking in mitigating HE in martensitic medium‐Mn steels. Paint baking at 180 °C for 20 min reduced the diffusible H content absorbed during austenitizing from ∼0.12 to 0.04 mass ppm. Subsequent room-temperature aging nearly eliminated diffusible H, resulting in H‐free specimens. The as-austenitized specimen underwent premature failure during tensile deformation due to diffusible H absorbed during austenitizing, whereas the H-free austenitized specimen exhibited a typical tensile flow curve without premature failure. Comparisons between H-free austenitized and paint-baked specimens revealed that paint baking increased yield strength through ɛ carbide formation and enhanced ductility by stabilizing retained austenite, delaying its transformation into martensite. Under identical H-charging conditions, the paint-baked specimens exhibited lower diffusible H content and higher non-diffusible H content, significantly improving HE resistance. Thermal desorption analysis revealed that H atoms trapped within ε carbides were released at 300–420 °C during their decomposition into cementite. Thus, the activation energy for peak 2 (225.2 kJ/mol) does not represent the activation energy for H desorption from ε carbides or retained austenite but rather the activation energy for the formation of cementite from ε carbides. |
| format | Article |
| id | doaj-art-c8aa1a68aeae4c3285b1418809e70858 |
| institution | Kabale University |
| issn | 2238-7854 |
| language | English |
| publishDate | 2025-07-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Journal of Materials Research and Technology |
| spelling | doaj-art-c8aa1a68aeae4c3285b1418809e708582025-08-20T03:34:13ZengElsevierJournal of Materials Research and Technology2238-78542025-07-01373832384510.1016/j.jmrt.2025.07.082Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steelJin-Young Lee0Hyun-Bin Jeong1Won Hui Jo2Jae Bok Seol3Young-Kook Lee4Department of Materials Science and Engineering, Yonsei University, Seoul, 03722, Republic of KoreaDepartment of Materials Science and Engineering, Yonsei University, Seoul, 03722, Republic of KoreaSchool of Materials Science and Engineering, Kookmin University, Seoul, 02707, Republic of KoreaSchool of Materials Science and Engineering, Kookmin University, Seoul, 02707, Republic of KoreaDepartment of Materials Science and Engineering, Yonsei University, Seoul, 03722, Republic of Korea; Graduate Institute of Ferrous & Eco Materials Technology, Pohang University of Science and Technology, Pohang, 37673, Republic of Korea; Corresponding author. Department of Materials Science and Engineering, Yonsei University, Seoul, 03722, Republic of Korea.Martensitic medium‐Mn steels have attracted significant attention for their excellent ultimate tensile strength, high ductility, and low austenitizing temperatures but remain susceptible to hydrogen embrittlement (HE). In this study, we investigated the role of ε carbides formed during paint baking in mitigating HE in martensitic medium‐Mn steels. Paint baking at 180 °C for 20 min reduced the diffusible H content absorbed during austenitizing from ∼0.12 to 0.04 mass ppm. Subsequent room-temperature aging nearly eliminated diffusible H, resulting in H‐free specimens. The as-austenitized specimen underwent premature failure during tensile deformation due to diffusible H absorbed during austenitizing, whereas the H-free austenitized specimen exhibited a typical tensile flow curve without premature failure. Comparisons between H-free austenitized and paint-baked specimens revealed that paint baking increased yield strength through ɛ carbide formation and enhanced ductility by stabilizing retained austenite, delaying its transformation into martensite. Under identical H-charging conditions, the paint-baked specimens exhibited lower diffusible H content and higher non-diffusible H content, significantly improving HE resistance. Thermal desorption analysis revealed that H atoms trapped within ε carbides were released at 300–420 °C during their decomposition into cementite. Thus, the activation energy for peak 2 (225.2 kJ/mol) does not represent the activation energy for H desorption from ε carbides or retained austenite but rather the activation energy for the formation of cementite from ε carbides.http://www.sciencedirect.com/science/article/pii/S2238785425017405Martensitic steelMedium-Mn steelε carbidesPaint bakingHydrogen embrittlement |
| spellingShingle | Jin-Young Lee Hyun-Bin Jeong Won Hui Jo Jae Bok Seol Young-Kook Lee Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel Journal of Materials Research and Technology Martensitic steel Medium-Mn steel ε carbides Paint baking Hydrogen embrittlement |
| title | Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel |
| title_full | Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel |
| title_fullStr | Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel |
| title_full_unstemmed | Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel |
| title_short | Hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium-Mn steel |
| title_sort | hydrogen desorption mechanism associated with ε carbide decomposition in martensitic medium mn steel |
| topic | Martensitic steel Medium-Mn steel ε carbides Paint baking Hydrogen embrittlement |
| url | http://www.sciencedirect.com/science/article/pii/S2238785425017405 |
| work_keys_str_mv | AT jinyounglee hydrogendesorptionmechanismassociatedwithecarbidedecompositioninmartensiticmediummnsteel AT hyunbinjeong hydrogendesorptionmechanismassociatedwithecarbidedecompositioninmartensiticmediummnsteel AT wonhuijo hydrogendesorptionmechanismassociatedwithecarbidedecompositioninmartensiticmediummnsteel AT jaebokseol hydrogendesorptionmechanismassociatedwithecarbidedecompositioninmartensiticmediummnsteel AT youngkooklee hydrogendesorptionmechanismassociatedwithecarbidedecompositioninmartensiticmediummnsteel |