Repairing crack in Cu-Cr-Zr alloy towards forging mechanical properties via friction stir processing and aging treatment
As an essential part of continuous casting, Cu-Cr-Zr alloy molds are susceptible to cracking due to molten steel erosion, stress corrosion, and fatigue failure caused by high-temperature gradient, posing significant challenges to repair efforts. Here, Cu-Cr-Zr alloy plates with 2 mm in-depth and 1 m...