Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5
The article presents the welding technology of a "Guide bushing - propeller shaft" type made of AlMg5 material and the problems that arise during welding depending on the way of obtaining the product (cast or rolled) and the chemical composition. The components have thicknesses between...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
THOT Publishing House
2025-03-01
|
| Series: | Journal of Research and Innovation for Sustainable Society |
| Subjects: | |
| Online Access: | https://jriss.4ader.ro/wp-content/uploads/2025/04/2.-G-Garleanu-D-Garleanu-C-Borda-C-Luchian-WELDING-TECHNOLOGIES-FOR-ALUMINUM-ALLOY-NAVAL-PARTS-PROPELLER-SHAFT-GUIDE-BUSHING-MADE-OF-ALMG5.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1849701343831261184 |
|---|---|
| author | Gabriel Gârleanu Delia Gârleanu Claudia Borda Cornelia Luchian |
| author_facet | Gabriel Gârleanu Delia Gârleanu Claudia Borda Cornelia Luchian |
| author_sort | Gabriel Gârleanu |
| collection | DOAJ |
| description | The article presents the welding technology of a "Guide bushing - propeller shaft"
type made of AlMg5 material and the problems that arise during welding depending on the way
of obtaining the product (cast or rolled) and the chemical composition. The components have
thicknesses between 20 – 40 mm and their welding raises some problems related to the welding
temperature and its maintenance during welding. Defects that appeared during welding, pores,
cracks, breaks and others are presented. These defects occurred not due to the parameters of the
welding regime but due to the way the casting was performed (gravitational and low temperature)
and the presence of copper in the alloy. After checking the chemical composition, an attempt
was made to remove the pores from the surface and near the surface, but without obtaining a
corresponding result. The solution to this problem was to change the semi-finished product as a
type of production. In conclusion, parts made by welding from cast aluminum alloys must first
be carefully checked for non-destructiveness, microcracks and granulation (especially the degree
of porosity) so that these factors do not become crack primers.
|
| format | Article |
| id | doaj-art-bcbe4b08ed864d02bff5e1360031bf57 |
| institution | DOAJ |
| issn | 2668-0416 |
| language | English |
| publishDate | 2025-03-01 |
| publisher | THOT Publishing House |
| record_format | Article |
| series | Journal of Research and Innovation for Sustainable Society |
| spelling | doaj-art-bcbe4b08ed864d02bff5e1360031bf572025-08-20T03:17:58ZengTHOT Publishing HouseJournal of Research and Innovation for Sustainable Society2668-04162025-03-01712230Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5Gabriel Gârleanu0Delia Gârleanu 1Claudia Borda 2Cornelia Luchian 3National University of Science and Technology POLITEHNICA Bucharest, RomaniaNational University of Science and Technology POLITEHNICA Bucharest, RomaniaNational University of Science and Technology POLITEHNICA Bucharest, RomaniaNational University of Science and Technology POLITEHNICA Bucharest, RomaniaThe article presents the welding technology of a "Guide bushing - propeller shaft" type made of AlMg5 material and the problems that arise during welding depending on the way of obtaining the product (cast or rolled) and the chemical composition. The components have thicknesses between 20 – 40 mm and their welding raises some problems related to the welding temperature and its maintenance during welding. Defects that appeared during welding, pores, cracks, breaks and others are presented. These defects occurred not due to the parameters of the welding regime but due to the way the casting was performed (gravitational and low temperature) and the presence of copper in the alloy. After checking the chemical composition, an attempt was made to remove the pores from the surface and near the surface, but without obtaining a corresponding result. The solution to this problem was to change the semi-finished product as a type of production. In conclusion, parts made by welding from cast aluminum alloys must first be carefully checked for non-destructiveness, microcracks and granulation (especially the degree of porosity) so that these factors do not become crack primers. https://jriss.4ader.ro/wp-content/uploads/2025/04/2.-G-Garleanu-D-Garleanu-C-Borda-C-Luchian-WELDING-TECHNOLOGIES-FOR-ALUMINUM-ALLOY-NAVAL-PARTS-PROPELLER-SHAFT-GUIDE-BUSHING-MADE-OF-ALMG5.pdfweldingaluminiumcracksalloy casting |
| spellingShingle | Gabriel Gârleanu Delia Gârleanu Claudia Borda Cornelia Luchian Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 Journal of Research and Innovation for Sustainable Society welding aluminium cracks alloy casting |
| title | Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 |
| title_full | Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 |
| title_fullStr | Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 |
| title_full_unstemmed | Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 |
| title_short | Welding technologies for aluminum alloy naval parts - propeller shaft guide bushing made of ALMG5 |
| title_sort | welding technologies for aluminum alloy naval parts propeller shaft guide bushing made of almg5 |
| topic | welding aluminium cracks alloy casting |
| url | https://jriss.4ader.ro/wp-content/uploads/2025/04/2.-G-Garleanu-D-Garleanu-C-Borda-C-Luchian-WELDING-TECHNOLOGIES-FOR-ALUMINUM-ALLOY-NAVAL-PARTS-PROPELLER-SHAFT-GUIDE-BUSHING-MADE-OF-ALMG5.pdf |
| work_keys_str_mv | AT gabrielgarleanu weldingtechnologiesforaluminumalloynavalpartspropellershaftguidebushingmadeofalmg5 AT deliagarleanu weldingtechnologiesforaluminumalloynavalpartspropellershaftguidebushingmadeofalmg5 AT claudiaborda weldingtechnologiesforaluminumalloynavalpartspropellershaftguidebushingmadeofalmg5 AT cornelialuchian weldingtechnologiesforaluminumalloynavalpartspropellershaftguidebushingmadeofalmg5 |