Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW
The effect of processing parameters on the mechanical and metallurgical properties of dissimilar joints of AA6082–AA6061 produced by friction stir welding was analysed in this study. Different FSW samples were produced by varying the welding speeds of the tool as 50 and 62 mm/min and by varying the...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2013-04-01
|
| Series: | Fracture and Structural Integrity |
| Subjects: | |
| Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero24/numero_24_art_16.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832569287070449664 |
|---|---|
| author | H. S. Patil S. N. Soman |
| author_facet | H. S. Patil S. N. Soman |
| author_sort | H. S. Patil |
| collection | DOAJ |
| description | The effect of processing parameters on the mechanical and metallurgical properties of dissimilar joints of AA6082–AA6061 produced by friction stir welding was analysed in this study. Different FSW samples were produced by varying the welding speeds of the tool as 50 and 62 mm/min and by varying the alloy positioned on the advancing side of the tool. In all the experiments the rotating speed is fixed at 1600rpm. All the welds were produced perpendicularly to the rolling direction for both the alloys. Microhardness (HV) and tensile tests performed at room temperature were used to evaluate the mechanical properties of the joints. In order to analyse the microstructural evolution of the material, the weld’s cross-sections were observed optically and SEM observations were made of the fracture surfaces. The corrosion tests of base alloy and welded joints were carried out in 3.5%NaCl solution at a room temperature. Corrosion current and potential were determined using potentiostatic polarization measurements. It was found that the corrosion rates of welded joints were higher than that of base alloy. |
| format | Article |
| id | doaj-art-bc437f6cf0f0433183511a93aeca3596 |
| institution | Kabale University |
| issn | 1971-8993 |
| language | English |
| publishDate | 2013-04-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj-art-bc437f6cf0f0433183511a93aeca35962025-02-02T22:34:03ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932013-04-01724151160Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSWH. S. PatilS. N. SomanThe effect of processing parameters on the mechanical and metallurgical properties of dissimilar joints of AA6082–AA6061 produced by friction stir welding was analysed in this study. Different FSW samples were produced by varying the welding speeds of the tool as 50 and 62 mm/min and by varying the alloy positioned on the advancing side of the tool. In all the experiments the rotating speed is fixed at 1600rpm. All the welds were produced perpendicularly to the rolling direction for both the alloys. Microhardness (HV) and tensile tests performed at room temperature were used to evaluate the mechanical properties of the joints. In order to analyse the microstructural evolution of the material, the weld’s cross-sections were observed optically and SEM observations were made of the fracture surfaces. The corrosion tests of base alloy and welded joints were carried out in 3.5%NaCl solution at a room temperature. Corrosion current and potential were determined using potentiostatic polarization measurements. It was found that the corrosion rates of welded joints were higher than that of base alloy.http://www.gruppofrattura.it/pdf/rivista/numero24/numero_24_art_16.pdfFSWAluminium alloys AA6082-AA6061Mechanical and metallurgical characterization |
| spellingShingle | H. S. Patil S. N. Soman Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW Fracture and Structural Integrity FSW Aluminium alloys AA6082-AA6061 Mechanical and metallurgical characterization |
| title | Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW |
| title_full | Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW |
| title_fullStr | Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW |
| title_full_unstemmed | Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW |
| title_short | Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW |
| title_sort | effect of weld parameter on mechanical and metallurgical properties of dissimilar joints aa6082 aa6061 in t6 condition produced by fsw |
| topic | FSW Aluminium alloys AA6082-AA6061 Mechanical and metallurgical characterization |
| url | http://www.gruppofrattura.it/pdf/rivista/numero24/numero_24_art_16.pdf |
| work_keys_str_mv | AT hspatil effectofweldparameteronmechanicalandmetallurgicalpropertiesofdissimilarjointsaa6082aa6061int6conditionproducedbyfsw AT snsoman effectofweldparameteronmechanicalandmetallurgicalpropertiesofdissimilarjointsaa6082aa6061int6conditionproducedbyfsw |