Influence of graphene nanoplatelets (GNPs) and aluminum-carbon layered double hydroxides (Al-C LDH) in polypropylene matrix of hybrid composite structures on the microstructure and mechanical performances
In this study, a polypropylene (PP) matrix was reinforced with ultra-fine graphene nanoplatelets (GNPs), aluminum-carbon layered double hydroxides (Al-C LDHs), and calcium carbonate (CaCO3) as hybrid reinforcements, along with polypropylene grafted maleic anhydride (PP-g-MA) compatibilizers to creat...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
AIMS Press
2024-10-01
|
| Series: | AIMS Materials Science |
| Subjects: | |
| Online Access: | https://www.aimspress.com/article/doi/10.3934/matersci.2024043 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In this study, a polypropylene (PP) matrix was reinforced with ultra-fine graphene nanoplatelets (GNPs), aluminum-carbon layered double hydroxides (Al-C LDHs), and calcium carbonate (CaCO3) as hybrid reinforcements, along with polypropylene grafted maleic anhydride (PP-g-MA) compatibilizers to create a novel thermoplastic-based hybrid composite polymer. The hybrid composite consisted of varying weight percentages of GNPs (ranging from 0.5 to 2.0 wt% in increments of 0.5), 2wt% Al-C LDH, 2wt % CaCO3, and 5wt % PP-g-MA. The bulk samples were manufactured using twin-screw extrusion followed by vertical injection molding. The developed hybrid composites were characterized using high-resolution scanning electron microscopy (HRSEM) for microstructural analysis, X-ray diffraction (XRD) for phase identification, X-ray photoelectron spectroscopy (XPS) for compositional analysis, and Fourier-transform infrared spectroscopy (FTIR) for functional group identification. Thermogravimetric analysis (TGA) was performed to assess thermal stability, crystallization, and melting behavior. Mechanical tests, including tensile, compressive, and three-point bending, were conducted to evaluate mechanical properties, while a low-velocity impact test assessed impact resistance. The results showed that the hybrid composite with a PP matrix embedded with 1.5 wt% GNPs, 2 wt% Al-C LDH, and 2 wt% CaCO3 exhibited improved mechanical properties, achieving an ultimate tensile strength of approximately 45 MPa. This enhancement is attributed to the effective interconnection, bonding, and cross-linking of the reinforcements with the PP matrix, facilitating efficient load transfer, which makes it suitable for structural applications. |
|---|---|
| ISSN: | 2372-0484 |