Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates
In order to investigate the causes of white stripe defects on the surface of 1100 aluminum plates during the anodizing process，chemical composition analysis， macroscopic morphology analysis， surface roughness analysis， scanning electron microscopy (SEM)， energy dispersive spectroscopy (EDS) analysis...
Saved in:
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Department of Materials Protection
2025-01-01
|
| Series: | Cailiao Baohu |
| Subjects: | |
| Online Access: | http://www.mat-pro.com/fileup/1001-1560/PDF/20250118.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1850204883639074816 |
|---|---|
| author | YANG Shuyu, ZHU Ranran, CHEN Yunan, QIAN Weifeng, LI Xiulei, ZHANG Xi, HAN Yi |
| author_facet | YANG Shuyu, ZHU Ranran, CHEN Yunan, QIAN Weifeng, LI Xiulei, ZHANG Xi, HAN Yi |
| author_sort | YANG Shuyu, ZHU Ranran, CHEN Yunan, QIAN Weifeng, LI Xiulei, ZHANG Xi, HAN Yi |
| collection | DOAJ |
| description | In order to investigate the causes of white stripe defects on the surface of 1100 aluminum plates during the anodizing process，chemical composition analysis， macroscopic morphology analysis， surface roughness analysis， scanning electron microscopy (SEM)， energy dispersive spectroscopy (EDS) analysis and X-ray diffraction (XRD) analysis were conducted to study the white stripe defects on the surface of the anodized 1100 aluminum plates.Results showed that the types， quantities and area fractions of AlFeSi phases in the white stripe defect areas were fewer than those in the normal areas.After anodizing fewer pits and corrosion holes caused by the AlFeSi phases were found in the white stripe defect areas compared to the normal areas.The surface roughness was also smaller in the defect areas than in the normal areas，which led to less diffuse reflection under natural light in the white stripe defect areas than in the normal areas， making them appear brighter and whiter compared to the normal areas. |
| format | Article |
| id | doaj-art-b9a6bf76926140769f7bc8c8acbdd28c |
| institution | OA Journals |
| issn | 1001-1560 |
| language | zho |
| publishDate | 2025-01-01 |
| publisher | Editorial Department of Materials Protection |
| record_format | Article |
| series | Cailiao Baohu |
| spelling | doaj-art-b9a6bf76926140769f7bc8c8acbdd28c2025-08-20T02:11:12ZzhoEditorial Department of Materials ProtectionCailiao Baohu1001-15602025-01-0158114915410.16577/j.issn.1001-1560.2025.0018Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum PlatesYANG Shuyu, ZHU Ranran, CHEN Yunan, QIAN Weifeng, LI Xiulei, ZHANG Xi, HAN Yi0(1.Suzhou Branch， Chinalco Materials Application Research Institute Co.， Ltd.， Suzhou 215026， China；2.Chinalco Materials Application Research Institute Co.， Ltd.， Beijing 102209， China)In order to investigate the causes of white stripe defects on the surface of 1100 aluminum plates during the anodizing process，chemical composition analysis， macroscopic morphology analysis， surface roughness analysis， scanning electron microscopy (SEM)， energy dispersive spectroscopy (EDS) analysis and X-ray diffraction (XRD) analysis were conducted to study the white stripe defects on the surface of the anodized 1100 aluminum plates.Results showed that the types， quantities and area fractions of AlFeSi phases in the white stripe defect areas were fewer than those in the normal areas.After anodizing fewer pits and corrosion holes caused by the AlFeSi phases were found in the white stripe defect areas compared to the normal areas.The surface roughness was also smaller in the defect areas than in the normal areas，which led to less diffuse reflection under natural light in the white stripe defect areas than in the normal areas， making them appear brighter and whiter compared to the normal areas.http://www.mat-pro.com/fileup/1001-1560/PDF/20250118.pdf1100 aluminum plate； anodizing； white stripe |
| spellingShingle | YANG Shuyu, ZHU Ranran, CHEN Yunan, QIAN Weifeng, LI Xiulei, ZHANG Xi, HAN Yi Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates Cailiao Baohu 1100 aluminum plate； anodizing； white stripe |
| title | Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates |
| title_full | Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates |
| title_fullStr | Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates |
| title_full_unstemmed | Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates |
| title_short | Research and Analysis of the Causes of White Stripe Defects in the Anodizing Process of 1100 Aluminum Plates |
| title_sort | research and analysis of the causes of white stripe defects in the anodizing process of 1100 aluminum plates |
| topic | 1100 aluminum plate； anodizing； white stripe |
| url | http://www.mat-pro.com/fileup/1001-1560/PDF/20250118.pdf |
| work_keys_str_mv | AT yangshuyuzhuranranchenyunanqianweifenglixiuleizhangxihanyi researchandanalysisofthecausesofwhitestripedefectsintheanodizingprocessof1100aluminumplates |