Corrosion properties of aluminized 16Mo3 steel
Chromium-molybdenum steel (16Mo3) is widely used in petroleum, gas, automotive, and construction industries due to its good oxidation resistance and mechanical properties at moderately elevated temperatures. The aim of the research was to evaluate the corrosion susceptibility of 16Mo3 steel in hot r...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Belgrade, Technical Faculty, Bor
2023-01-01
|
| Series: | Journal of Mining and Metallurgy. Section B: Metallurgy |
| Subjects: | |
| Online Access: | https://doiserbia.nb.rs/img/doi/1450-5339/2023/1450-53392300008K.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Chromium-molybdenum steel (16Mo3) is widely used in petroleum, gas, automotive, and construction industries due to its good oxidation resistance and mechanical properties at moderately elevated temperatures. The aim of the research was to evaluate the corrosion susceptibility of 16Mo3 steel in hot rolled and aluminized states. Aluminization was performed by diffusion pack aluminization process at 900°C/2h and 730°C/4h, respectively. Electrochemical corrosion testing included measuring open circuit potential (EOCP), linear polarization resistance (LPR), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) in potassium phosphate buffer (KH2PO4, pH = 7). Optical microscopy (OM), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS) were used for surface layer microstructure characterization before and after corrosion tests. It was demonstrated that corrosion resistance of aluminized steel increased substantially. Corrosion properties were related to the structure and properties of intermetallic phase (FeAl, FeAl2 and Fe2Al5) that formed on the surface of 16Mo3 steel. |
|---|---|
| ISSN: | 1450-5339 2217-7175 |