Quantitative spatial mapping of distorted state phases during the metal-insulator phase transition for nanoscale VO2 engineering
Vanadium dioxide (VO2) material, known for changing physical properties due to metal-insulator transition (MIT) near room temperature, has been reported to undergo a phase change depending on the strain. This fact can be a significant problem for nanoscale devices in VO2, where the strain field cove...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor & Francis Group
2023-12-01
|
| Series: | Science and Technology of Advanced Materials |
| Subjects: | |
| Online Access: | https://www.tandfonline.com/doi/10.1080/14686996.2022.2150525 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Vanadium dioxide (VO2) material, known for changing physical properties due to metal-insulator transition (MIT) near room temperature, has been reported to undergo a phase change depending on the strain. This fact can be a significant problem for nanoscale devices in VO2, where the strain field covers a large area fraction, spatially non-uniform, and the amount of strain can vary during the MIT process. Direct measurement of the strain field distribution during MIT is expected to establish a methodology for material phase identification. We have demonstrated the effectiveness of geometric phase analysis (GPA), high-resolution transmission electron microscopy techniques, and transmission electron diffraction (TED). The GPA images show that the nanoregions of interest are under tensile strain conditions of less than 0.4% as well as a compressive strain of about 0.7% (Rutile phase VO2[100] direction), indicating that the origin of the newly emerged TED spots in MIT contains a triclinic phase. This study provides a substantial understanding of the strain-temperature phase diagram and strain engineering strategies for effective phase management of nanoscale VO2. |
|---|---|
| ISSN: | 1468-6996 1878-5514 |