Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating
CaCO3-epoxy composite coatings containing different qualities of nano-Al2O3 were successfully prepared. Infrared spectroscopy was used to verify whether the nano- Al2O3 was modified successfully and scanning electron microscopic (SEM) pictures were taken to study the inner morphology of the composit...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2016-06-01
|
| Series: | Nanomaterials and Nanotechnology |
| Subjects: | |
| Online Access: | http://www.intechopen.com/journals/nanomaterials_and_nanotechnology/study-of-nano-alumina-impact-on-the-performance-of-a-caco3-epoxy-composite-coating |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1849397221352538112 |
|---|---|
| author | Li Chen Fenglei Chenli Zhi Luo Ying Xin |
| author_facet | Li Chen Fenglei Chenli Zhi Luo Ying Xin |
| author_sort | Li Chen |
| collection | DOAJ |
| description | CaCO3-epoxy composite coatings containing different qualities of nano-Al2O3 were successfully prepared. Infrared spectroscopy was used to verify whether the nano- Al2O3 was modified successfully and scanning electron microscopic (SEM) pictures were taken to study the inner morphology of the composite coatings. When tested by the hydraulic universal material testing system (MTS), it was found that the mechanical performances of composite coatings worsened after added nano-Al2O3. Thermo gravimetric analysis (TGA) and differential scanning calorimetry (DSC) indicated that the thermal stability of composite coatings increased after nano-Al2O3 was added; the abrasion resistance test explained that wear resistance also improved. Finally, it was found that the comprehen‐ sive performances of composite coatings for anticorrosion and adhesive strength were best after being tested under 63MPa and 165°C in an autoclave, when added at 10wt% nano-Al2O3. |
| format | Article |
| id | doaj-art-af9498f8a21a465fbbc9cf9fddb83047 |
| institution | Kabale University |
| issn | 1847-9804 |
| language | English |
| publishDate | 2016-06-01 |
| publisher | Wiley |
| record_format | Article |
| series | Nanomaterials and Nanotechnology |
| spelling | doaj-art-af9498f8a21a465fbbc9cf9fddb830472025-08-20T03:39:05ZengWileyNanomaterials and Nanotechnology1847-98042016-06-01639http://dx.doi.org/10.5772/6378651238Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite CoatingLi ChenFenglei ChenliZhi LuoYing XinCaCO3-epoxy composite coatings containing different qualities of nano-Al2O3 were successfully prepared. Infrared spectroscopy was used to verify whether the nano- Al2O3 was modified successfully and scanning electron microscopic (SEM) pictures were taken to study the inner morphology of the composite coatings. When tested by the hydraulic universal material testing system (MTS), it was found that the mechanical performances of composite coatings worsened after added nano-Al2O3. Thermo gravimetric analysis (TGA) and differential scanning calorimetry (DSC) indicated that the thermal stability of composite coatings increased after nano-Al2O3 was added; the abrasion resistance test explained that wear resistance also improved. Finally, it was found that the comprehen‐ sive performances of composite coatings for anticorrosion and adhesive strength were best after being tested under 63MPa and 165°C in an autoclave, when added at 10wt% nano-Al2O3.http://www.intechopen.com/journals/nanomaterials_and_nanotechnology/study-of-nano-alumina-impact-on-the-performance-of-a-caco3-epoxy-composite-coatingEpoxy Composite CoatingNano-aluminaAnticorrosionAdhesive Strength |
| spellingShingle | Li Chen Fenglei Chenli Zhi Luo Ying Xin Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating Nanomaterials and Nanotechnology Epoxy Composite Coating Nano-alumina Anticorrosion Adhesive Strength |
| title | Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating |
| title_full | Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating |
| title_fullStr | Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating |
| title_full_unstemmed | Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating |
| title_short | Study of Nano-alumina Impact on the Performance of a CaCO3-Epoxy Composite Coating |
| title_sort | study of nano alumina impact on the performance of a caco3 epoxy composite coating |
| topic | Epoxy Composite Coating Nano-alumina Anticorrosion Adhesive Strength |
| url | http://www.intechopen.com/journals/nanomaterials_and_nanotechnology/study-of-nano-alumina-impact-on-the-performance-of-a-caco3-epoxy-composite-coating |
| work_keys_str_mv | AT lichen studyofnanoaluminaimpactontheperformanceofacaco3epoxycompositecoating AT fengleichenli studyofnanoaluminaimpactontheperformanceofacaco3epoxycompositecoating AT zhiluo studyofnanoaluminaimpactontheperformanceofacaco3epoxycompositecoating AT yingxin studyofnanoaluminaimpactontheperformanceofacaco3epoxycompositecoating |