Ultrafine grained W–Ti alloys prepared by spark plasma sintering
The W–Ti alloys with the Ti atomic fraction in the range of 15%~30% were prepared by spark plasma sintering in this paper. The phase composition, microstructure, and formation mechanism of the ultrafine grained W–Ti alloys with the different Ti content were studied. The results show that, the W–Ti a...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Powder Metallurgy Technology
2021-04-01
|
| Series: | Fenmo yejin jishu |
| Subjects: | |
| Online Access: | https://pmt.ustb.edu.cn/article/doi/10.19591/j.cnki.cn11-1974/tf.2019110008 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The W–Ti alloys with the Ti atomic fraction in the range of 15%~30% were prepared by spark plasma sintering in this paper. The phase composition, microstructure, and formation mechanism of the ultrafine grained W–Ti alloys with the different Ti content were studied. The results show that, the W–Ti alloys containing β1(Ti,W) phase and β2(Ti,W) phase can be prepared by spark plasma sintering at 1100 ℃ in 5 min. Under the combined action of Ti segregation and rapid sintering, the grain size of the centimeter-sized bulk samples is up to sub-micron scale, and the properties of the W–Ti alloys first increase and then decrease with the increase of Ti content. When the Ti atomic fraction is 25%, the relative density of the samples is (98.5±0.1) %, the average size of W grains is about (340±20) nm, and the hardness and compressive strength are HV (860±2) and (2600±10) MPa, respectively. |
|---|---|
| ISSN: | 1001-3784 |