Effects of Composition on Melt Fillability and Impact Resistance of TiAl Alloys for Thin-Blade Turbine Wheels: Laboratory Predictions and Product Verification
Scaling up the production of TiAl turbine wheels for passenger car turbochargers requires the fabrication of thin blades that are similar to those of nickel-based superalloys. To achieve this, the molten metal fillability and impact resistance of thin blades must be improved. In this study, the effe...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2025-04-01
|
| Series: | Metals |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2075-4701/15/5/474 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Scaling up the production of TiAl turbine wheels for passenger car turbochargers requires the fabrication of thin blades that are similar to those of nickel-based superalloys. To achieve this, the molten metal fillability and impact resistance of thin blades must be improved. In this study, the effects of composition on these properties are predicted using simple laboratory experiments with binary, ternary, and practical alloys and are then verified with actual turbine wheels. The melt fillability of the turbine wheel blade is predicted using the amount of molten metal passing through an Al<sub>2</sub>O<sub>3</sub>-1%SiO<sub>2</sub> mesh. The binary alloy exhibits the best fillability, which is reduced by the addition of Cr and Si. Charpy impact tests on as-cast materials at 25 and 850 °C show that the addition of Cr and Mn improves the impact resistance, but the addition of Nb, W, Mo and Si reduces it. Therefore, the molten metal fillability and/or impact resistance of practical TiAl alloys containing such additives owing to other requirements are low and require improvement for use in thin-blade turbine wheel applications. |
|---|---|
| ISSN: | 2075-4701 |