WC-Co-Ni cemented carbides with 90 wt.% WC and different Co/Ni ratios (WC-(1−x)Co-xNi, where x = 0, 1, 3, 5, 7 and 9 wt.%) were prepared by powder metallurgy method. The aim was to study the microstructure of these carbides, analyse their mechanical properties and investigate their corrosion resista...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Novi Sad
2025-06-01
|
| Series: | Processing and Application of Ceramics |
| Subjects: | |
| Online Access: | https://doiserbia.nb.rs/img/doi/1820-6131/2025/1820-61312502121X.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | WC-Co-Ni cemented carbides with 90 wt.% WC and different Co/Ni ratios (WC-(1−x)Co-xNi, where x = 0, 1, 3, 5, 7 and 9 wt.%) were prepared by powder metallurgy method. The aim was to study the microstructure of these carbides, analyse their mechanical properties and investigate their corrosion resistance and thus find the optimal Co/Ni ratio for the fabrication of reliable cutting tools. The results show that with the increase of Ni content, the grain size and inhomogeneity gradually increase. On the other hand, the hardness, wear resistance and flexural strength of WC-Co-Ni cemented carbides decrease. The fracture toughness firstly increases and then decreases while the corrosion resistance is enhanced. The WC-7Co-3Ni specimen had the best comprehensive mechanical properties compared to other composites. This, together with the improved corrosion and damage resistance, confirmed that the WC-7Co-3Ni composite could substantially extend the working life of shield machine tools. |
|---|---|
| ISSN: | 1820-6131 2406-1034 |