Microstructure and Mechanical Property of Hot-Pressed Al2O3-Ni-P Composites Using Ni-P-Coated Al2O3 Powders
Al2O3-Ni-P composite powders with Ni-P contents of 10.9, 14.4, and 20.4 wt.% were synthesized via the Ni-P electroless deposition process. The as-received Al2O3-Ni-P composite powders were composed of Ni-P particles and Ni-P coating layer. Some Ni-P particles randomly adhered to the Al2O3 powders, a...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2015-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2015/148657 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Al2O3-Ni-P composite powders with Ni-P contents of 10.9, 14.4, and 20.4 wt.% were synthesized via the Ni-P electroless deposition process. The as-received Al2O3-Ni-P composite powders were composed of Ni-P particles and Ni-P coating layer. Some Ni-P particles randomly adhered to the Al2O3 powders, and their particle diameter ranged from 5 nm to 20 nm. The thin Ni-P layer had about 5 nm thick amorphous structure and directly bonded with Al2O3 powders. Using the Ni-P-coated Al2O3 powders, a dense Al2O3-Ni-P composite can be successfully obtained using the hot press process at 1,350°C for 1 hour in an Ar atmosphere under an applied pressure of 30 MPa. The hot-pressed Al2O3-15 wt.% Ni-P composite showed excellent material properties. Its relative density, Vickers hardness, and fracture toughness were comparatively high: about 99.1%, 2,360 Hv, and 6 MPa·m1/2, respectively. The fracture surface of the hot-pressed Al2O3-Ni-P composite showed a semiductile mode due to the mixed intergranular and transgranular fracture mode. In particular, the fracture toughness of the hot-pressed Al2O3-15 wt.% Ni-P composite was strongly enhanced by the combined action of the crack branching and the crack deflection. |
|---|---|
| ISSN: | 1687-8434 1687-8442 |