Influence of Temperature on the Performance of LiNi1/3Co1/3Mn1/3O2 Prepared by High-Temperature Ball-Milling Method
Aiming at the preparation of high electrochemical performance LiNi1/3Co1/3Mn1/3O2 cathode material for lithium-ion battery, LiNi1/3Co1/3Mn1/3O2 was prepared with lithium carbonate, nickel (II) oxide, cobalt (II, III) oxide, and manganese dioxide as raw materials by high-temperature ball-milling meth...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2018-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2018/6842694 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Aiming at the preparation of high electrochemical performance LiNi1/3Co1/3Mn1/3O2 cathode material for lithium-ion battery, LiNi1/3Co1/3Mn1/3O2 was prepared with lithium carbonate, nickel (II) oxide, cobalt (II, III) oxide, and manganese dioxide as raw materials by high-temperature ball-milling method. Influence of ball-milling temperature was investigated in this work. It was shown that the fine LiNi1/3Co1/3Mn1/3O2 powder with high electrochemical performance can be produced by the high-temperature ball-milling process, and the optimal ball-milling temperature obtained in the current study was 750°C. Its initial discharge capacity was 146.0 mAhg−1 at the rate of 0.1 C, and over 50 cycles its capacity retention rate was 90.2%. |
|---|---|
| ISSN: | 1687-8434 1687-8442 |