Biaxial Flexural Strength and Vickers Hardness of 3D-Printed and Milled 5Y Partially Stabilized Zirconia
This study compares the mechanical properties of 5-mol% yttria partially stabilized zirconia (5Y-PSZ) materials, designed for 3D printing or milling. Three 5Y-PSZ materials were investigated: printed zirconia (PZ) and two milled zirconia materials, VITA-YZ-XT (MZ-1) and Cercon xt (MZ-2). PZ samples...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2025-01-01
|
| Series: | Journal of Functional Biomaterials |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2079-4983/16/1/36 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This study compares the mechanical properties of 5-mol% yttria partially stabilized zirconia (5Y-PSZ) materials, designed for 3D printing or milling. Three 5Y-PSZ materials were investigated: printed zirconia (PZ) and two milled zirconia materials, VITA-YZ-XT (MZ-1) and Cercon xt (MZ-2). PZ samples were made from a novel ceramic suspension via digital light processing and divided into three subgroups: PZ-HN-ZD (horizontal nesting, printed with Zipro-D Dental), PZ-VN-Z (vertical nesting, printed with Zipro-D Dental) and PZ-VN-Z (vertical nesting, printed with Zipro Dental). Key outcomes included biaxial flexural strength (ISO 6872) and Vickers hardness (<i>n</i> ≥ 23 samples/subgroup). Microstructure and grain size were analyzed using light and scanning electron microscopy. Printed specimens exhibited biaxial flexural strengths of 1059 ± 178 MPa (PZ-HN-ZD), 797 ± 135 MPa (PZ-VN-ZD), and 793 ± 75 MPa (PZ-VN-Z). Milled samples showed strengths of 745 ± 96 MPa (MZ-1) and 928 ± 87 MPa (MZ-2). Significant differences (α = 0.05) were observed, except between vertically printed groups and MZ-1. Vickers hardness was highest for PZ-VN-Z (HV0.5 = 1590 ± 24), followed by MZ-1 (HV0.5 = 1577 ± 9) and MZ-2 (HV0.5 = 1524 ± 4), with significant differences, except between PZ and MZ-1. PZ samples had the smallest grain size (0.744 ± 0.024 µm) compared to MZ-1 (0.820 ± 0.042 µm) and MZ-2 (1.023 ± 0.081 µm). All materials met ISO 6872 standards for crowns and three-unit prostheses in posterior regions. |
|---|---|