FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE
During the drilling operation,the drill pipe near the surface usually stands the largest tension and torsion.Stress concentration is relatively serious in the upset transitional section of the drill pipe,where initiation of fatigue cracks,washouts and even fracture accidents are prone to happening.B...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Office of Journal of Mechanical Strength
2017-01-01
|
| Series: | Jixie qiangdu |
| Subjects: | |
| Online Access: | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2017.04.031 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1841535184107732992 |
|---|---|
| author | ZHAO GuangHui ZHAO Li TANG Song LI Ju |
| author_facet | ZHAO GuangHui ZHAO Li TANG Song LI Ju |
| author_sort | ZHAO GuangHui |
| collection | DOAJ |
| description | During the drilling operation,the drill pipe near the surface usually stands the largest tension and torsion.Stress concentration is relatively serious in the upset transitional section of the drill pipe,where initiation of fatigue cracks,washouts and even fracture accidents are prone to happening.Based on the actual operating loads of G105 drill pipe,which is near the well head of an ultra-deep vertical well,finite element model of the inner upset transitional section containing a circumferential semielliptical surface crack was established.The fracture characters of the cracked model were simulated under the combination of tension and torsion.For different loading ratios and crack depths,the transition aspect ratios are determined and variation laws of the dimensionless stress intensity factor are fitted along with the crack propagating.This paper provides a basis for study on the fatigue life of drill pipe which is subjected to combined loads. |
| format | Article |
| id | doaj-art-6f95474cd36d4afcb68e0bac736397ab |
| institution | Kabale University |
| issn | 1001-9669 |
| language | zho |
| publishDate | 2017-01-01 |
| publisher | Editorial Office of Journal of Mechanical Strength |
| record_format | Article |
| series | Jixie qiangdu |
| spelling | doaj-art-6f95474cd36d4afcb68e0bac736397ab2025-01-15T02:34:12ZzhoEditorial Office of Journal of Mechanical StrengthJixie qiangdu1001-96692017-01-013992092630599427FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPEZHAO GuangHuiZHAO LiTANG SongLI JuDuring the drilling operation,the drill pipe near the surface usually stands the largest tension and torsion.Stress concentration is relatively serious in the upset transitional section of the drill pipe,where initiation of fatigue cracks,washouts and even fracture accidents are prone to happening.Based on the actual operating loads of G105 drill pipe,which is near the well head of an ultra-deep vertical well,finite element model of the inner upset transitional section containing a circumferential semielliptical surface crack was established.The fracture characters of the cracked model were simulated under the combination of tension and torsion.For different loading ratios and crack depths,the transition aspect ratios are determined and variation laws of the dimensionless stress intensity factor are fitted along with the crack propagating.This paper provides a basis for study on the fatigue life of drill pipe which is subjected to combined loads.http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2017.04.031Drill pipeInner upset transitional sectionSemi-elliptical surface crackFracture characterStress intensity factor |
| spellingShingle | ZHAO GuangHui ZHAO Li TANG Song LI Ju FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE Jixie qiangdu Drill pipe Inner upset transitional section Semi-elliptical surface crack Fracture character Stress intensity factor |
| title | FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE |
| title_full | FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE |
| title_fullStr | FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE |
| title_full_unstemmed | FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE |
| title_short | FRACTURE CHARACTERS OF SURFACE CRACK IN THE INNER UPSET TRANSITIONAL SECTION OF DRILL PIPE |
| title_sort | fracture characters of surface crack in the inner upset transitional section of drill pipe |
| topic | Drill pipe Inner upset transitional section Semi-elliptical surface crack Fracture character Stress intensity factor |
| url | http://www.jxqd.net.cn/thesisDetails#10.16579/j.issn.1001.9669.2017.04.031 |
| work_keys_str_mv | AT zhaoguanghui fracturecharactersofsurfacecrackintheinnerupsettransitionalsectionofdrillpipe AT zhaoli fracturecharactersofsurfacecrackintheinnerupsettransitionalsectionofdrillpipe AT tangsong fracturecharactersofsurfacecrackintheinnerupsettransitionalsectionofdrillpipe AT liju fracturecharactersofsurfacecrackintheinnerupsettransitionalsectionofdrillpipe |