Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage
Slug catchers offer effectively multiphase flow management in the field of oil and gas industry. critical equipment required for isolates and confines liquid, gases, and solid particles in slugs under environmental conditions that observed to incoming production stream. This work examines the case s...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2024-11-01
|
| Series: | Heliyon |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S2405844024163384 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1850065288455782400 |
|---|---|
| author | Nuha Hadi Jasim Al Hasan Ali Talib khanjar |
| author_facet | Nuha Hadi Jasim Al Hasan Ali Talib khanjar |
| author_sort | Nuha Hadi Jasim Al Hasan |
| collection | DOAJ |
| description | Slug catchers offer effectively multiphase flow management in the field of oil and gas industry. critical equipment required for isolates and confines liquid, gases, and solid particles in slugs under environmental conditions that observed to incoming production stream. This work examines the case study that undergoes corrosion failure in vessels of slug catcher, concentrating on (H2S) damage, hardness, and microscopic corrosion in different locations. The methodology of this study involved visual inspections, hardness, and microscopic testing in order to evaluate the level of nature corrosion. The results refer that while the failure of corrosion pits present, there were not cracks, microcracks, stress corrosion cracking (SCC), or Hydrogen Induced Cracking (HIC) recognized in the structural of vessel. The structures of ferrite and pearlite of the HIC were presented in main components, and there are no cracks or microcracks detected. |
| format | Article |
| id | doaj-art-690e7b37fb2b4b3e8e35a7ccbc7be64d |
| institution | DOAJ |
| issn | 2405-8440 |
| language | English |
| publishDate | 2024-11-01 |
| publisher | Elsevier |
| record_format | Article |
| series | Heliyon |
| spelling | doaj-art-690e7b37fb2b4b3e8e35a7ccbc7be64d2025-08-20T02:49:02ZengElsevierHeliyon2405-84402024-11-011022e4030710.1016/j.heliyon.2024.e40307Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damageNuha Hadi Jasim Al Hasan0Ali Talib khanjar1Department of Engineering Materials University of Basrah, College of Engineering, Iraq; Corresponding author.Basrah Gas Company, Department of Inspection, IraqSlug catchers offer effectively multiphase flow management in the field of oil and gas industry. critical equipment required for isolates and confines liquid, gases, and solid particles in slugs under environmental conditions that observed to incoming production stream. This work examines the case study that undergoes corrosion failure in vessels of slug catcher, concentrating on (H2S) damage, hardness, and microscopic corrosion in different locations. The methodology of this study involved visual inspections, hardness, and microscopic testing in order to evaluate the level of nature corrosion. The results refer that while the failure of corrosion pits present, there were not cracks, microcracks, stress corrosion cracking (SCC), or Hydrogen Induced Cracking (HIC) recognized in the structural of vessel. The structures of ferrite and pearlite of the HIC were presented in main components, and there are no cracks or microcracks detected.http://www.sciencedirect.com/science/article/pii/S2405844024163384 |
| spellingShingle | Nuha Hadi Jasim Al Hasan Ali Talib khanjar Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage Heliyon |
| title | Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage |
| title_full | Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage |
| title_fullStr | Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage |
| title_full_unstemmed | Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage |
| title_short | Investigation of slug catcher vessel degradation by hydrogen sulfide (H2S) damage |
| title_sort | investigation of slug catcher vessel degradation by hydrogen sulfide h2s damage |
| url | http://www.sciencedirect.com/science/article/pii/S2405844024163384 |
| work_keys_str_mv | AT nuhahadijasimalhasan investigationofslugcatchervesseldegradationbyhydrogensulfideh2sdamage AT alitalibkhanjar investigationofslugcatchervesseldegradationbyhydrogensulfideh2sdamage |