Effects of Silica Aerogel Content on the Properties of Waterborne Organic Thermal Insulation Coatings
In order to cope with the emergence of energy conservation and consumption reduction initiatives, we used an acrylic emulsion (as the adhesive), combined with silica aerogel (SA) and hollow glass microsphere (HGM) fillers, to synthesize thermal insulation coatings, which were found to have low therm...
Saved in:
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2025-07-01
|
| Series: | Gels |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2310-2861/11/7/547 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In order to cope with the emergence of energy conservation and consumption reduction initiatives, we used an acrylic emulsion (as the adhesive), combined with silica aerogel (SA) and hollow glass microsphere (HGM) fillers, to synthesize thermal insulation coatings, which were found to have low thermal conductivity and excellent thermal insulation properties. These waterborne coatings are environmentally friendly and were synthesized without organic solvents. Comprehensive testing verified that the coatings met practical requirements. Specifically, the addition of 18% SA resulted in minimal thermal conductivity (0.0433 W/m·K), the lowest density (0.177 g/cm<sup>3</sup>), as well as a reduced gross calorific value. At a heating surface temperature of 200 °C, the 5 mm coating’s cooling surface temperature was 108.7 °C, yielding a 91.3 °C temperature difference and demonstrating remarkable thermal insulation performance. Furthermore, the coatings showed favorable results in terms of water resistance, corrosion resistance, wear resistance, and adhesion, achieving satisfactory engineering standards. In this work, the influence of different contents of SA on various properties of the coating was studied, with the aim of providing a reference for the modulation of the comprehensive performance of SA thermal insulation coatings. |
|---|---|