High cycle torsional fatigue properties of 17-4PH stainless steel
Sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle fatigue regime. Fatigue crack initiation and small crack growth behaviors were observed during fatigue testing and fractographic investigations were performed. The results are compared to the data...
Saved in:
Main Authors: | , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Gruppo Italiano Frattura
2016-07-01
|
Series: | Fracture and Structural Integrity |
Subjects: | |
Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero37/numero_37_art_14.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Sensitivity to small defects under torsional fatigue loading condition is examined in the high cycle
fatigue regime. Fatigue crack initiation and small crack growth behaviors were observed during fatigue testing
and fractographic investigations were performed. The results are compared to the data obtained in the uniaxial
fatigue tests, which allows the effect of biaxial stresses on the surface of material to be discussed. Finally, an
approach for predicting the fatigue limit of 17-4PH stainless steel under torsional and tension-compression
fatigue loadings is presented. |
---|---|
ISSN: | 1971-8993 1971-8993 |