Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels
The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that inves...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2013-04-01
|
| Series: | Fracture and Structural Integrity |
| Online Access: | https://www.fracturae.com/index.php/fis/article/view/107 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832544259548381184 |
|---|---|
| author | I. S. Raju N. F. Knight K. Song D. R. Phillips |
| author_facet | I. S. Raju N. F. Knight K. Song D. R. Phillips |
| author_sort | I. S. Raju |
| collection | DOAJ |
| description | The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses. |
| format | Article |
| id | doaj-art-407abb3b76784f1cba5b04cd341c8013 |
| institution | Kabale University |
| issn | 1971-8993 |
| language | English |
| publishDate | 2013-04-01 |
| publisher | Gruppo Italiano Frattura |
| record_format | Article |
| series | Fracture and Structural Integrity |
| spelling | doaj-art-407abb3b76784f1cba5b04cd341c80132025-02-03T10:40:13ZengGruppo Italiano FratturaFracture and Structural Integrity1971-89932013-04-0151510.3221/IGF-ESIS.15.05Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panelsI. S. RajuN. F. KnightK. SongD. R. PhillipsThe Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses.https://www.fracturae.com/index.php/fis/article/view/107 |
| spellingShingle | I. S. Raju N. F. Knight K. Song D. R. Phillips Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels Fracture and Structural Integrity |
| title | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_full | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_fullStr | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_full_unstemmed | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_short | Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels |
| title_sort | fracture mechanics analyses of the slip side joggle regions of wing leading edge panels |
| url | https://www.fracturae.com/index.php/fis/article/view/107 |
| work_keys_str_mv | AT israju fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT nfknight fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT ksong fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels AT drphillips fracturemechanicsanalysesoftheslipsidejoggleregionsofwingleadingedgepanels |