The Effect of annealing temperature on the optical properties of (Cu2S)100-x( SnS2 )x thin films
Thin films of (Cu2S)100-x( SnS2 )x at X=[ 30,40, &50)]% with thickness (0.9±0.03)µm , had been prepared by chemical spray pyrolysis method on glass substrates at 573 K. These films were then annealed under low pressure of(10-2) mbar ,373)423&473)K for one hour . This research includes , stu...
Saved in:
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Baghdad, College of Science for Women
2014-06-01
|
| Series: | مجلة بغداد للعلوم |
| Subjects: | |
| Online Access: | http://bsj.uobaghdad.edu.iq/index.php/BSJ/article/view/2676 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Thin films of (Cu2S)100-x( SnS2 )x at X=[ 30,40, &50)]% with thickness (0.9±0.03)µm , had been prepared by chemical spray pyrolysis method on glass substrates at 573 K. These films were then annealed under low pressure of(10-2) mbar ,373)423&473)K for one hour . This research includes , studying the the optical properties of (Cu2S)100-x-(SnS2)x at X=[ 30,40, &50)]% .Moreover studying the effect of annealing on their optical properties , in order to fabricate films with high stability and transmittance that can be used in solar cells. The transmittance and absorbance spectra had been recorded in the wavelength range (310 - 1100) nm in order to study the optical properties . It was found that these films had direct optical band gap which decreases with the increasing SnS2 ratio , while it increasing with the increase in the annealing temperature at all ratio |
|---|---|