Fracture Behavior and Cracking Mechanism of Rock Materials Containing Fissure-Holes Under Brazilian Splitting Tests
Fractures and voids are widely distributed in slope rock masses. These defects promote crack initiation and propagation, ultimately leading to rock mass failure. Investigating their damage evolution mechanisms and strength characteristics is of significant importance for slope hazard prevention. A n...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2025-05-01
|
| Series: | Applied Sciences |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2076-3417/15/10/5592 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Fractures and voids are widely distributed in slope rock masses. These defects promote crack initiation and propagation, ultimately leading to rock mass failure. Investigating their damage evolution mechanisms and strength characteristics is of significant importance for slope hazard prevention. A numerical simulation study of Brazilian splitting tests on disk samples containing prefabricated holes and fractures was conducted using the Finite Element Method with Cohesive Zone Modeling (FEM-CZM) in ABAQUS by embedding zero-thickness cohesive elements within the finite element model. This 2021 study analyzed the effects of fracture angle and length on tensile strength and crack propagation characteristics. The results revealed that when the fracture angle is small, cracks initiate near the fracture and propagate and intersect radially as the load increases, ultimately leading to specimen failure, with the crack coalescence pattern exhibiting local closure. As the fracture angle increases, the initiation location of the crack shifts. With an increase in fracture length, the crack initiation position may transfer to other parts of the fracture or near the hole, and longer fractures may result in more complex coalescence patterns and local closure phenomena. During the tensile and stable failure stages, the load–displacement curves of samples with different fracture angles and lengths exhibit similar trends. However, the fracture angle has a notable impact on the curve during the shear failure stage, while the fracture length significantly affects the peak value of the curve. Furthermore, as displacement increases, the proportion of tensile failure undergoes a process of rapid decline, slow rise, and then rapid decline again before stabilizing, with the fracture angle having a significant influence on the proportion of tensile failure. Lastly, as the fracture angle and length increase, the number of damaged cohesive elements shows an upward trend. This study provides novel perspectives on the tensile behavior of fractured rock masses through the FEM-CZM approach, contributing to a fundamental understanding of the strength characteristics and crack initiation mechanism of rocks under tensile loading conditions. |
|---|---|
| ISSN: | 2076-3417 |