Interaction of ZG-refractory with mold flux and ambient air
Zirconia graphite refractory is used in continuous casting of steel. Slag corrosion resistance influence on time of casting. With factorial experiment 25-1 influence mixture of refractory (content of graphite, silicon carbide, boron carbide) on oxidation resistance and interaction with mould powder...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Ural Federal University
2014-12-01
|
| Series: | Chimica Techno Acta |
| Subjects: | |
| Online Access: | https://chimicatechnoacta.ru/article/view/722 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1849309317182783488 |
|---|---|
| author | A. V. Jagovcev N. V. Obabkov |
| author_facet | A. V. Jagovcev N. V. Obabkov |
| author_sort | A. V. Jagovcev |
| collection | DOAJ |
| description | Zirconia graphite refractory is used in continuous casting of steel. Slag corrosion resistance influence on time of casting. With factorial experiment 25-1 influence mixture of refractory (content of graphite, silicon carbide, boron carbide) on oxidation resistance and interaction with mould powder (C/S = 1, F = 8 %) at 1400 °C. Boron carbide is better antioxidant than silicon carbide. Boron carbide 3 % mass decrease slag corrosion resistance of ZG-refractory. The thicknesses de-carbonized layer are within 1–7 mm Additives of boron carbide and silicon carbide reduce the thickness of the oxidized layer. It was established experimentally that the boron carbide has the best antioxidant properties than silicon carbide therefore, in the study circolatorio materials action SiC less effective than B4C. |
| format | Article |
| id | doaj-art-122d962ef90d41c2bb46e21b656c1957 |
| institution | Kabale University |
| issn | 2411-1414 |
| language | English |
| publishDate | 2014-12-01 |
| publisher | Ural Federal University |
| record_format | Article |
| series | Chimica Techno Acta |
| spelling | doaj-art-122d962ef90d41c2bb46e21b656c19572025-08-20T03:54:11ZengUral Federal UniversityChimica Techno Acta2411-14142014-12-011311111610.15826/chimtech.2014.1.3.7221125Interaction of ZG-refractory with mold flux and ambient airA. V. Jagovcev0N. V. Obabkov1Уральский федеральный университет, ЕкатеринбургУральский федеральный университет, ЕкатеринбургZirconia graphite refractory is used in continuous casting of steel. Slag corrosion resistance influence on time of casting. With factorial experiment 25-1 influence mixture of refractory (content of graphite, silicon carbide, boron carbide) on oxidation resistance and interaction with mould powder (C/S = 1, F = 8 %) at 1400 °C. Boron carbide is better antioxidant than silicon carbide. Boron carbide 3 % mass decrease slag corrosion resistance of ZG-refractory. The thicknesses de-carbonized layer are within 1–7 mm Additives of boron carbide and silicon carbide reduce the thickness of the oxidized layer. It was established experimentally that the boron carbide has the best antioxidant properties than silicon carbide therefore, in the study circolatorio materials action SiC less effective than B4C.https://chimicatechnoacta.ru/article/view/722цирконистографитовый материалогнеупоршлаккарбид кремниякарбид бораантиокислительные свойства |
| spellingShingle | A. V. Jagovcev N. V. Obabkov Interaction of ZG-refractory with mold flux and ambient air Chimica Techno Acta цирконистографитовый материал огнеупор шлак карбид кремния карбид бора антиокислительные свойства |
| title | Interaction of ZG-refractory with mold flux and ambient air |
| title_full | Interaction of ZG-refractory with mold flux and ambient air |
| title_fullStr | Interaction of ZG-refractory with mold flux and ambient air |
| title_full_unstemmed | Interaction of ZG-refractory with mold flux and ambient air |
| title_short | Interaction of ZG-refractory with mold flux and ambient air |
| title_sort | interaction of zg refractory with mold flux and ambient air |
| topic | цирконистографитовый материал огнеупор шлак карбид кремния карбид бора антиокислительные свойства |
| url | https://chimicatechnoacta.ru/article/view/722 |
| work_keys_str_mv | AT avjagovcev interactionofzgrefractorywithmoldfluxandambientair AT nvobabkov interactionofzgrefractorywithmoldfluxandambientair |