Typical continuous annealing technology of cold-rolled 700 MPa ultra-high strength low-alloy steel
In order to develop a new generation cold-rolled ultra-high strength low-alloy steel, continuous annealing experiments of a Ti-0.12%, Nb-0.076% cold-rolled ultra-high strength low-alloy steel were done on a continuous annealing test machine. The influence of annealing temperature on the phase compos...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Science Press
2015-02-01
|
| Series: | 工程科学学报 |
| Subjects: | |
| Online Access: | http://cje.ustb.edu.cn/article/doi/10.13374/j.issn2095-9389.2015.02.008 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In order to develop a new generation cold-rolled ultra-high strength low-alloy steel, continuous annealing experiments of a Ti-0.12%, Nb-0.076% cold-rolled ultra-high strength low-alloy steel were done on a continuous annealing test machine. The influence of annealing temperature on the phase composition, grain size, and mechanical properties of the steel was investigated at four dif-ferent annealing temperature ranges from 760℃ to 830℃. The final composition is ferrite and a small amount of bainite under 800℃ annealing and 400℃ over-aging conditions, the ferrite grain size is about 1.4 μn, and the yield strength reaches up to 700 MPa. A large number of nanometer size sub-crystal structures, a small number of dislocations, and nano-Ti and Nb precipitates are observed by scanning electron microscopy and transmission electron microscopy. Those microstructures improve the strength a lot. |
|---|---|
| ISSN: | 2095-9389 |